镍基合金电焊条(SMAW Electrodes for Ni Base Alloys)
产品牌号 | 分类标准及标号 | 基本化学成份典型值(%) | 热处理 | σ0.2 | σb | δ5 | AKW | |||||||||||
AWS A5.11/A5.4* | DIN1736 | C | Mn | Si | Cr | Ni | Mo | Nb | Fe | Co | 其它 | MPa | MPa | % | ℃ | J | ||
13/65 TTW 150 | ENiCrMo-6 | ≈EL-NiCr 13 Mo 6 Fe | 0.05 | 3.5 | 0.5 | 15.0 | Bal. | 5.5 | 1.1 | <6.0 | W:1.2 | AW | 410 | 660 | 35 | -196 | 60 | |
30/40 E | ≈E383-15* | EL-NiCr 28 Mo | ≤0.03 | 2.7 | <0.5 | 28.0 | 36.0 | 3.8 | Cu:1.8 | AW | 350 | 550 | 30 | +20 | 75 | |||
30/40 EW | ≈E383-17* | EL-NiCr 28 Mo | ≤0.03 | 1.5 | <0.9 | 28.0 | 36.0 | 4.3 | Cu:1.8 | AW | 350 | 550 | 30 | +20 | 50 | |||
30/50 | - | EL-NiCr 28 W | 0.50 | 2.5 | 1.3 | 28.5 | 49.0 | W:4.5 | AW | 450 | 650 | 5 | - | - | ||||
617 | ≈ENiCrCoMo-1 | EL-NiCr 21 Co 12 Mo | ≤0.08 | <0.5 | 0.7 | 21.0 | 余量 | 9.0 | 12.0 | Al:1.0 | AW | 400 | 700 | 30 | +20 | 100 | ||
625 | ≈ENiCrMo-3 | EL-NiCr 19 Nb | <0.05 | 4.0 | 0.4 | 19.5 | 余量 | 9.5 | 3.3 | <2.0 | AW | 380 | 620 | 35 | -269 | 50 | ||
690 | ENiCrFe-7 | (EL-NiCr 29 Fe) | 0.04 | 2.5 | 0.5 | 29.5 | 余量 | 1.5 | 9.0 | ≤0.1 | AW | 350 | 600 | 35 | +20 | 80 | ||
Nicro 82 | ≈ENiCrFe-3 | EL-NiCr 19 Nb | <0.05 | 4.0 | 0.4 | 19.5 | 余量 | 2.0 | <4.0 | AW | 380 | 620 | 35 | -269 | 50 | |||
Nicro 182 | ENiCrFe-3 | EL-NiCr 16 FeMn | ≤0.05 | 6.5 | <0.5 | 16.0 | 余量 | 2.0 | ≤6.0 | AW | 350 | 620 | 35 | -196 | 70 | |||
Nimo C | ≈E NiCrMo-7 | EL-NiCr 19 Mo 15 | <0.02 | 1.5 | <0.3 | 19.0 | 余量 | 15.0 | ≤1.5 | V:0.3 | AW | 450 | 700 | 40 | +20 | 60 | ||
Nimo CW | ≈E NiCrMo-7 | EL-NiCr 19 Mo 15 | <0.02 | 1.0 | <0.3 | 19.0 | 余量 | 15.0 | ≤1.5 | V:0.3 | AW | 450 | 700 | 40 | +20 | 60 | ||
Nimo C 24 | ENiCrMo-13 | EL-NiCr 22 Mo 16 | <0.02 | <0.5 | 0.1 | 23.0 | 余量 | 16.0 | ≤1.5 | AW | 420 | 700 | 40 | +20 | 60 | |||